Título : | COMPARATIVE STUDY OF NI-W/CEO2, NI-W/Y-AL2O3 AND NI-W/HT CATALYSTS FOR H2 PRODUCTION BY STEAM REFORMING OF BIOETHANOL |
Autor : | MESSINA FERNANDEZ, SARAH RUTH HERNANDEZ ROSALES, IRMA PAZ FERNANDEZ MADRIGAL, ARTURO |
Palabras clave : | catalizadores soporte en CeO vapor de etanol deposicion de carbono efecto fotovoltaico impregnacion metodos de precipitacion catalysts CeO support ethanol vapor carbon deposition photovoltaic effect impregnation precipitation methods |
Fecha de publicación : | 10-dic-2011 |
Editorial : | Química Hoy |
Resumen : | Los catalizadores de Ni-W soportados en CeO2, Al2O3 e hidrotalcita (HT) fueron estudiados en el reformado al vapor de etanol a 500-650 C. El CeO2 y el HT fueron sintetizados por métodos de impregnación y coprecipitación directa, respectivamente. Se utilizó Al2O3 comercial. El contenido de níquel varió de 10, 15 y 30% con 1% W. El catalizador que presentó la mayor actividad catalítica y selectividad al hidrógeno fue 10% Ni-W/HT. La conversión a etanol fue del 100% y las selectividades a H2, CH4, CO2 y CO fueron de 75, 5,78, 0,37 y 18,85%, respectivamente, a una temperatura de 500 °C. Además, estos catalizadores mostraron buena estabilidad con respecto a la deposición de carbono y baja selectividad hacia la producción de C2H4. Estas son características deseables para los catalizadores a ser usados en la producción de hidrógeno para aplicaciones de celdas de combustible. |
Descripción : | Ni-W catalysts supported on CeO2, Al2O3, and hydrotalcite (HT) were studied in the steam reforming of ethanol at 500-650 C. The CeO2, and HT were synthesized by impregnation and direct coprecipitation methods, respectively. Commercial Al2O3 was used. Nickel content was varied from 10, 15 and 30% with 1% W. The catalyst that presented the highest catalytic activity and selectivity to hydrogen was 10% Ni-W/HT. Conversion to ethanol was 100% and selectivities to H2, CH4, CO2, and CO were 75, 5.78, 0.37 and 18.85%, respectively, at a temperature of 500 °C. Moreover, these catalysts showed good stability with respect to carbon deposition and low selectivity towards C2H4 production. These are desirable features for catalysts to be used in hydrogen production for fuel cell applications. |
URI : | http://dspace.uan.mx:8080/jspui/handle/123456789/1555 |
ISSN : | 2007-1183 |
Aparece en las colecciones: | Artículos científicos |
Ficheros en este ítem:
Fichero | Descripción | Tamaño | Formato | |
---|---|---|---|---|
COMPARATIVE STUDY OF NI-W_CEO2, NI-W_Y-AL2O3 AND NI-W_HT CATALYSTS FOR H2 PRODUCTION BY STEAM REFORMING OF BIOETHANOL.pdf | 5.27 MB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.